How To Reduce The Breakage Rate Of Stainless Steel Wire

The impact load of stainless steel wire will be caused under the influence of severe impact in the process of use. Once the accumulated value exceeds the allowable working stress range, there will be tensile fracture, which will undoubtedly shorten the service life of stainless steel wire. In addition to this reason, wire clamping and insufficient lubrication may also break the stainless steel wire, affecting its performance. How to fundamentally reduce the wire breakage rate of stainless steel wire can be started from the following points:

During the drawing process of stainless steel wire, some particles will fall off and get stuck in the compression area of the die, resulting in wire breakage. To solve this problem, the lubricant must be changed periodically to reduce the wire breakage rate; The problem of winding or wire clamping on the take-up wheel will also cause wire breakage. Therefore, when controlling the starting tension of the foundation, it is necessary to wind several more wires on the constant speed wheel carefully, and the wire clamping of stainless steel wire cannot occur; The incorrect size of the die used on the machine will also cause confusion in the proportion of the normal compression ratio, resulting in wire breakage; If there is water cut-off or oil end phenomenon during the operation of the machine, it will also cause the wire break problem, which needs to ensure the cooling and lubrication of each die, and periodically remove the whole set of dies for inspection to avoid the wire break problem caused by the imbalance of compression ratio.